Author: Shin, Minkyu; Yoon, Jinho; Yi, Chanyong; Lee, Taek; Choi, Jeong-Woo
Title: Flexible HIV-1 Biosensor Based on the Au/MoS(2) Nanoparticles/Au Nanolayer on the PET Substrate Document date: 2019_7_26
ID: 0trs364m_13
Snippet: The conformation and composition of the synthesized MoS 2 NPs were investigated by TEM and EDS analysis. As shown in Figure 2a , the TEM images indicated that the synthesized MoS 2 NPs were structured as well-dispersed nanospheres. The EDS and EDS mapping results are shown in Figure 2b and Figure S1 . EDS and EDS mapping images showed that the ratio of molybdenum (Mo) and sulfur (S) was approximately 1:2, which matched the theoretical composition.....
Document: The conformation and composition of the synthesized MoS 2 NPs were investigated by TEM and EDS analysis. As shown in Figure 2a , the TEM images indicated that the synthesized MoS 2 NPs were structured as well-dispersed nanospheres. The EDS and EDS mapping results are shown in Figure 2b and Figure S1 . EDS and EDS mapping images showed that the ratio of molybdenum (Mo) and sulfur (S) was approximately 1:2, which matched the theoretical composition of MoS 2 . Additionally, the average size of MoS 2 (concentration: 1 mg/mL) was investigated by dynamic light scattering (DLS). The measured DLS data indicated that 80.37% of synthesized MoS 2 were about 200 nm to 300 nm, and 19.63% of MoS 2 were over 300 nm (Figure 2c
Search related documents:
Co phrase search for related documents- average size and EDS analysis: 1
- dynamic light and EDS analysis: 1, 2
- dynamic light and TEM EDS analysis: 1
- EDS analysis and mapping result: 1
- EDS analysis and TEM EDS analysis: 1, 2, 3
Co phrase search for related documents, hyperlinks ordered by date